贮氢电极合金粉末
我们可以提供不同需求的贮氢电极合金粉末
可以根据客户的要求调整化学或者物理特征。
贮氢合金是在一定温度和压力条件下可以可逆地大量吸收和放出氢气的材料。在金属氢化物/镍电池（MH/Ni电池）中，贮氢合金作为负极，是该电池的关键材料。
1.化学成分
| 类型 | C | L | T | S | E | ||
| 分子式 | ABx | ABx | ABx | ABx | ABx | ||
| x=5.1±0.10 | x=5.1±0.10 | x=4.85±0.10 | x=5.15±0.10 | x=5.25±0.10 | |||
| 主元素 | Mm(TRE)(%) | 32.7±1.0 | 32.6±1.0 | 34.0±1.0 | 32.4±1.0 | 32.2±1.0 | |
| Co(%) | 10.0±0.5 | 10.0±0.5 | 10.2±0.5 | 5.0~9.0 | 3.0~7.0 | ||
| 杂质 (%) | O | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | |
| Fe | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | ||
| Mg | ≤0.03 | ≤0.03 | ≤0.03 | ≤0.03 | ≤0.03 | ||
| Zn | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ||
| Ca | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ||
| C | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ||
| Pb | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.02 | ||
| 电化学性能 | 循环寿命(100%DOD) | ≥500 | ≥600 | ≥400 | ≥500 | ≥500 | |
| 电化学容量 | ≥320mAh/g | ≥310mAh/g | ≥300mAg/g | ≥320mAh/g | ≥300mAh/g | ||
| 电压的单位(1.2V/1.0V) | ≥80% | ≥80% | ≥85% | ≥80% | ≥80% | ||
| 氢吸收和释放性能 | 氢吸收能力(Hab/m) | 10atm | >0.90H/M | >0.90H/M | >0.85H/M | >0.90H/M | >0.85H/M |
| 3atm | >0.80H/M | >0.80H/M | >0.65H/M | >0.80H/M | >0.78H/M | ||
| 平衡氢压( H/M=0.4) | 0.4±0.1atm | 0.35±0.1atm | 1.3±0.1atm | 0.5±0.1atm | 0.45±0.1atm | ||
| 高原性能 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ||
| 推荐用法 | 适合生产高容量电池 | 适合生产长寿命电池 | 适合生产低温性能电池 | 适用于动力电池生产 | 适合经济电池生产 | ||
2.物理特性
| 推荐用干制法的粒径 | 推荐用湿制法的粒径 | ||
| LSA D50 | 68±5um | 44±5um | |
| 大小筛分析 | -100目(150um) | 100% | 100% |
| -140目(106um) | ≥97% | ≥99% | |
| -200目(75um) | ≥65% | ≥85% | |
| -325目(45um) | ≥30% | ≥60% | |
| -400目(38um) | ≤23% | ≥40% | |
| 表观密度 | ≥3.4g/cm3 | ≥3.2g/cm3 | |
| 振实密度 | ≥4.4g/cm3 | ≥4.4g/cm3 | |